| Applicable Materials | : | Copper/Tin/Zinc/Nickel/Sheet Lead |
| Capacity | : | 8 oz |
| Color | : | Tan/Gold to Black |
| Composition | : | 10 to 25% Zinc Chloride, 10 to 25% Ammonium Chloride, <10% Zinc Oxide, Tin, <1% Antimony |
| Container Type | : | Jar |
| Flammability Rating | : | 1 |
| Flash Point | : | >399 deg F |
| Form | : | Paste |
| Melting Range | : | Copper/Tin/Zinc/Nickel/Sheet Lead Applicable Materials |
| Odor/Scent | : | Petroleum |
| Series | : | 95/5 |
| Specific Gravity | : | 1.59 |
| VOC Content | : | 0 g/L |
| Warranty | : | Limited |
RectorSeal® NOKORODE® Pre-Tinning Paste Flux, Series: 95/5, 8 oz, Jar, 0 g/L VOC, Paste, Composition: 10 to 25% Zinc Chloride, 10 to 25% Ammonium Chloride, <10% Zinc Oxide, Tin, <1% Antimony, Tan/Gold to Black, Petroleum, >399 deg F Flash, 120 to 150 deg F Melting, Flammability: 1, 1.59 Specific Gravity, Applicable Materials: Copper/Tin/Zinc/Nickel/Sheet Lead
- Produces excellent, leak-free soldered joints
- Lead-free - formula is safe for use on potable systems
- Cleans, pre-tins and fluxes
- Great for large diameter fittings or faster soldering of small diameter fittings because it automatically tins before a high temperature is reached
- Cuts waste
- Very low scorching or burning
- Very low corrosive properties prevents pitting
- Very low spattering
- Excellent wetting ability allows solder to flow easily and uniformly into joints
- Smooth stable paste for easy brush on application
- Contains small amount of 95/5 solder powder
- 2 years minimum shelf life
- Wt/gal at 77 deg F: 8.44 +/- 0.5 lb/gal
- Do not use on magnesium or aluminum
- Recommended for 95/5 or 50/50 solder applications